Top to Bottom Solution Deposition of Inorganic Solar Modules

ABSTRACT

A technique is described depositing a new formula of indium and tin salt solutions as a precursor to form a solid transparent indium tin oxide (ITO) film on non-conductive solid substrates. The utilization of this new composition of matter prompted the discovery of a method for preparing the first top-to-bottom completely solution processed solar cell. The specific patterning of the liquid-processed ITO precursor solution and the subsequent layers of a solar cell outlined here also demonstrate a unique way to connect solution processed (as opposed to deposited using vacuum techniques) solar cells in series and in parallel. Also contemplated are similar compositions capable of forming zinc tin oxide (ZTO), indium oxide (IO), indium zinc oxide (IZO), cadmium tin oxide (CTO), aluminum zinc oxide (AZO), or zinc oxide (ZO).

BACKGROUND

Commercial indium tin oxide (ITO) films are used in a variety ofoptoelectronics, digital displays, touch panels, organic light-emittingdiodes, optical coatings, gas sensors, electrochemical cells, and solarcells also termed photovoltaic (PV) devices. ITO is known for its hightransmittance of visible light (80-90%) while maintaining high sheetconductivity (8-12 Ω/sq) and thermal stability (T<400° C.) (see ref. 2).Drawbacks to ITO include the limited freedom and high cost ofdeposition. ITO films are commonly deposited under specific atmosphericconditions by atomic sputter deposition onto glass or quartz attemperatures above 450° C., or the conventional solution process shownin FIG. 1. Recently, a report on solution based ITO demonstratedspin-cast films of indium nitrate and tin chloride dissolved in asolvent with a fuel and oxidizer (see ref. 1). Upon heating totemperatures ranging from 250-450° C., an exothermic reaction isinitiated that produces extreme local temperatures hot enough to producecrystalline ITO (the combustion process shown in FIG. 1). In aniterative layer-by-layer process alternating between heating and spincoating, the ITO film can be deposited to the desired thickness. Thesefilms suffer from low transmittance, however, and contain a yellowcolored solid material. In experiments with solar cells, they were alsofound to have lower conductivity than reported in the literature. Inorder to produce high quality ITO films that are both transparent tovisible light (>80%) and conductive (<400 Ω/sq), a new formula forsolution deposition of ITO is desired.

An answer to this problem would allow a solution ITO procedure to beapplied to solar cells to produce the first all-solution inorganic solarcell. Solution processing of inorganic solar cells has been investigatedby several groups (see refs. 3-9). Notable is the ITO/CdTe/CdSe/Alstructure first demonstrated by Alivisatos et al. (2005) (ref. 7) whereboth CdTe and CdSe were spin coated onto ITO from solution ofnanocrystals. Since then, other groups have included solution processedPbS, PbSe, and CuInS₂ among others. These inorganic nanocrystal coreswere synthesized with an organic capping ligand to facilitate thematerial solubility. The inorganic core contains the cadmiumchalcogenide semiconductor with a narrow band gap which can absorbvisible light and produce an electron/hole pair as a result of theabsorbed photon. These charges can be collected by the ITO or Al contactto produce light driven power. While some of these devices employ asolution processed contact (i.e. AgNWs (ref. 10), Ag paint (ref. 11),graphite (ref. 12), each of these examples; however, still use vacuumsputtered transparent conductive oxides (TCOs), (refs. 4, 6, and 10-18),e-beam evaporated metal contacts (ref. 4, 6, and 13-18) or metal contactsubstrates where the device was built on patterned copper (ref. 19). Itis not believed that a complete PV device has been deposited viasolution onto non-conductive substrates.

BRIEF SUMMARY

Described herein is a technique for depositing a new formula of indiumand tin salt solutions as a precursor to form a solid transparent indiumtin oxide (ITO) film on non-conductive solid substrates. The utilizationof this new composition of matter prompted the discovery of a method forpreparing the first top-to-bottom completely solution processed solarcell. The specific patterning of the liquid-processed ITO precursorsolution and the subsequent layers of a solar cell outlined here alsodemonstrate a unique way to connect solution processed (as opposed todeposited using vacuum techniques) solar cells in series and in parallelto amplify light driven voltage and current, respectively based on novellayer-by-layer masking patterns.

One embodiment is a composition for forming indium tin oxide (ITO), thecomposition consisting essentially of: a solution of a tin salt, anindium salt, ammonium nitrate, ammonium hydroxide, and a solvent of2-methoxyethanol or water, wherein, upon heating a thin film formed fromthe solution, the composition is capable of forming a substantiallytransparent ITO film having a sheet resistance of <300 Ω/sq.

Another embodiment is a composition for forming metal oxides, thecomposition consisting essentially of: a solution of (a) a nitrate ofzinc, indium, cadmium, or aluminum, (b) optionally tin chloride, (c)ammonium nitrate, and (d) ammonium hydroxide, all in a solvent of2-methoxyethanol or water, wherein the composition is capable of formingzinc tin oxide (ZTO), indium oxide (IO), indium zinc oxide (IZO),cadmium tin oxide (CTO), aluminum zinc oxide (AZO), or zinc oxide (ZO).

In a further embodiment, a method of creating indium tin oxide (ITO)includes forming a layer of a solution consisting essentially of a tinchloride, an indium(III) nitrate, ammonium nitrate, ammonium hydroxide,and a solvent of 2-methoxyethanol or water; and heating the layer toform ITO having a sheet resistance of <300 Ω/sq

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a scheme illustrating low-temperature solution processingof metal oxide films compared to conventional solution deposition

FIGS. 2A and 2B show absorbance of a combustion ITO film preparedaccording to ref. 1 after layered deposition at various indium molarconcentrations (A) and resistance of the film as a function of layersfor various concentrations (B).

FIGS. 3A through 3D show characterization of the ITO prepared asdescribed herein with UV/Vis Transmittance [A], x-ray diffraction (XRD)[B], and scanning electron microscopy (SEM) [C] with optimization of theSn content showing film resistance plotted as a function of Sn to In wt.% in the film for increasing numbers of layers (1-6) [D].

FIG. 4 shows photovoltaic I-V curves of ITO|CdSe|CdTe|Au single devicesbuilt on commercial ITO, ITO made as described herein (“NRL ITO”), andLiterature ITO.

FIGS. 5A through 5H illustrate module design showing masking pattern forsolution processed solar cells with ITO (Layer 1), n-type CdSe (Layer2), p-type CdTe (Layer 3), gold contact (Layer 4) and the completed celltop-down view and cross section view of completed layers (H). Thelayering process shows each individual layer (A,B,D,F) and the outlineof each layer as the module is built (C,E,G).

FIG. 6 illustrates an example of a sprayable panel onto a glasssubstrate consisting of 2-parallel circuits connected in series wherethe sprayable metal contact connects the 8-cell modules to amplifyvoltage and current.

FIG. 7A shows an X-ray diffraction pattern for In₂O₃ made as describedherein as compared to reference values. FIG. 7B shows an X-raydiffraction pattern for ZnO made as described herein as compared toreference values.

DETAILED DESCRIPTION Definitions

Before describing the present invention in detail, it is to beunderstood that the terminology used in the specification is for thepurpose of describing particular embodiments, and is not necessarilyintended to be limiting. Although many methods, structures and materialssimilar, modified, or equivalent to those described herein can be usedin the practice of the present invention without undue experimentation,the preferred methods, structures and materials are described herein. Indescribing and claiming the present invention, the following terminologywill be used in accordance with the definitions set out below.

As used in this specification and the appended claims, the singularforms “a”, “an,” and “the” do not preclude plural referents, unless thecontent clearly dictates otherwise.

As used herein, the term “and/or” includes any and all combinations ofone or more of the associated listed items.

As used herein, the term “about” when used in conjunction with a statednumerical value or range denotes somewhat more or somewhat less than thestated value or range, to within a range of ±10% of that stated.

Description

In this disclosure, a new formula for solution processed ITO withsuperior properties is described along with its use in a solar cell,preferably an all-inorganic solar cell. The freedom of solutionprocessing allows for the ability arrange the layers of a solar cell indifferent ways as desired. An efficient and easily producible maskingpattern for layer-by-layer deposition of a solar cell with solutionbased ITO, Au, Pt, or Ag is also described for spin or spray depositionof inorganic solar cells. The masking pattern can also be applied toother devices (solar cells, light detectors, light emitting diodes,etc.) with a special emphasis on enabling large area (from 1 μm² togreater than 1 m²) deposition on non-standard substrates which are notnecessarily flat, smooth, or easily manipulated.

Transparent Conductive Solution

Commercial ITO contains a range of ratios of indium to tin oxides, andmost common is 90% In₂O₃ to 10% SnO₂ by weight. With solutiondeposition, this ratio can be obtained easily along with a range ofother ratios, with an upper limit to the solubility of each metal saltin the solution, and a lower limit as low as desired or measurable. Theliterature method (ref. 1) for this calls for a molar ratio of[12.7:0.217:0.389:0.200:0.180:0.017] for [2-methoxyethanol(solvent):NH₄OH (pH stabilizer):acetylacetone (fuel):NH₄NO₃(oxidizer):indium:tin (metal)]. By combining these metal salts insolution with a fuel (acetylacetone or urea) and oxidizer, lowtemperature heating (150-350° C.) initiates a highly exothermiccombustion synthesis (Equation 1 example for zinc oxide combustionformation (ref. 1)).

3Zn(NO₃)₂.6H₂O_((s))+5CO(NH₂)₂→3ZnO_((s))8N_(2(g))+28G₂O_((g))+5CO_(2(g))

ΔH _(298K)=−2320.4 kJ and T _(ad)˜700° C.  Eq. 1

contaminated with highly absorbing yellow powder and overall highresistances (>1000 Ω/sq as seen in FIG. 2B). It is possible that theyellow colored powder consists of acetylacetone (ACAC) and In₂O₃residues and/or an indium-ACAC complex. Given that these compounds forma yellow solid upon heating, this leads to increased resistance in thefilm since these powders are not conductive. They also lead to increasedabsorbance in the visible region between 250-350 nm (FIG. 2A) whichwould account for the yellow color. The necessity for high transmittancein the visible region therefore requires that these reactions areavoided.

Surprisingly, the fuel (ACAC or urea) is not needed in this reaction andit was discovered that the fuel can be removed from the solution toproduce films with 30× lower resistivity. Along with other modificationsto the formula, the new mixture (Table 1) was developed that produceshighly transparent films of ITO that are also conductive (<300 Ω/sq).The fuel component of the prior art mixture is not required and iscontrary to the basic and novel characteristics of the new formula.However, it is possible to include dopants to improve electricalcharacteristics without disrupting the basic and novel characteristicsof the new formula. A typical film preparation includes spin coating thesolution at 4500 rpm and annealing at 380° C. for approximately 15 minfor each new layer.

TABLE 1 Comparison of molar concentrations (mol/L) of reagents used inthe literature method of ref. 1 and the optimized formula ConcentrationActual Ratio Amounts Concentrations (M) (New/ for New ReagentsLiterature New Literature) Solution SnCl₂•2H₂O 0.017 0.158 9.43 0.357 gIn(NO₃)₃•2.85 H₂O 0.180 0.832 4.63 2.93 g NH₄NO₃ 0.200 1.04 5.20 0.83 gNH₄OH 0.217 0.242 1.11 167 μL 2-methoxyethanol 12.68 12.68 1 10 mL ACAC0.3896 — — —

This iterative process builds the film thickness to approach the desiredconductivity (which increases with film thickness) while maintaininghigh transmittance (which decreases with film thickness). A subsequentlayer should not be heated longer than the previous layer since thiscauses cracking in the lower films. The material can also be spray castusing an airbrush at the same concentration as used for spin coating, orit can be diluted with solvent. Film quality is shown with SEM, XRD andUV/Vis in FIGS. 3A through 3C. The weight percent ratio of which isnormally 10%: 90%, respectively, in commercial ITO, was optimized byexperimentation. Surprisingly, it was discovered that 15% SnO₂ wasoptimal for this method (FIG. 3D). In embodiments, SnO₂ is present in anamount ranging from 14%-16% by weight, 13%-17% by weight, or 12%-18% byweight, with the remaining percent In₂O₃, measured with regard to thetotal weight of the hydrated forms of SnO₂ and In₂O₃ described inTable 1. It is not believed that the hydration state is critical, sothat, for example, equivalent amounts of anhydrous forms could be used.Furthermore, this new formula can be applied to other transparentconductive metal oxides such as zinc tin oxide (ZTO), indium oxide (IO),indium zinc oxide (IZO), cadmium tin oxide (CTO), aluminum zinc oxide(AZO), zinc oxide (ZO) to produce higher quality films by removingorganic residue from the ACAC ligands and reducing processing times.ITO, IQ IZO and ZO have been tested in the lab. FIG. 7A shows an X-raydiffraction pattern for In₂O₃ made as described herein as compared toreference values. FIG. 7B shows an X-ray diffraction pattern for ZnOmade as described herein as compared to reference values.

Replacing the 2-methoxyethanol solvent with water also met with somesuccess. The films were spun in the same manner; however, the glass waspre-treated with concentrated NaOH rinsing to create better adhesionbetween the hydrophobic glass and the water solution. This method asinitially performed was time-sensitive, and it was found that the metalsalts precipitate after 1 hour in solution. However, because the organiccontent of the metal oxide film appears detrimental to opticaltransmission and conductivity, an all aqueous system may be advantageousfor some applications. The SEM image (FIG. 3C inset) shows the H₂O-ITOsurface with larger grains than ITO prepared as described here(“NRL-ITO”), indicating the combustion process here leads to a morecontinuous film.

All-Solution all-Inorganic Solar Cell

The above-described new ITO formula (having <300 Ω/sq) was applied to aworking photovoltaic device to produce what is believed to be the firstall-solution all-inorganic solar cell. This was then compared to asimilar device built on commercial ITO (8-12 Ω/sq) and a separate devicebuilt on ITO made from the literature procedure (>10 kΩ/sq) with theconfiguration of ITO/CdSe/CdTe/Au. The I-V data (FIG. 4) measured with aKeithley 617 source meter under ˜1 sun illumination shows the dependenceof the resistance on the fill factor (FF=[I·V]/[I_(sc)·V_(oc)]).

The inverted slope of the I-V curve for the literature ITO sample isconsistent with high resistance on the ITO contact. The fill factor isimproved from FF=16% (Literature ITO) to 22% (NRL ITO) to 27%(Commercial ITO) in addition to an increase in the current and voltage,leading to a two-fold increase in device efficiency between LiteratureITO and NRL ITO. Therefore, not only does this new formula saveprocessing time (1 h vs. 5 h), it also leads to a higher quality film ofITO for improved properties for optoelectronic applications includingsolar cells, light detectors, and other devices.

Solution Processed Solar Cell Module Patterned Masks

Working solar cells were made using the solution processed ITO. Solarcells contain an active layer sandwiched between two metal contacts.Usually, a transparent conductive material (ITO, FTO) is purchased orvacuum deposited, followed by the active layers (semiconductors forinorganic cells or dyes for organic cells), and finally topped with anevaporated metal electrode to produce a solar cell (see ref. 7,incorporated by reference herein for disclosing methods of forming solarcells from solution). The ITO and metal serve as the anode and cathodefor the solar cell to produce a voltage/current during illumination witha light source. This produces light-driven power for one cell. Solarcell modules contain individual cells that are connected in series(ITO-cell 1 to metal-cell 2 to ITO-cell 3, etc.) in order to sum thevoltages of each cell. They can also be connected in parallel(metal-cell 1 to metal-cell 2 to metal-cell 3, etc.) to produce a sum ofthe photocurrents. A combination of series and parallel connections canbe used to produce a module with the desired voltage and current.

A technique was developed to pattern individual layers of a solutionprocessed solar cell in ambient air to add voltage and current with amask for spin-coated or spray cast solar cells. This pattern was thenapplied to an ITO/CdSe/CdTe/Au structure where all layers are solutionprocessed. However, a similar technique could also be applied tonon-solution processed solar cells, light detectors, or other electronicdevices. Layer 1 is a bottom contact patterned with ITO on glass. The3″×1″ module consists of 8 (or more) cells connected in series. Withthis configuration, the total voltage of the module is the sum of eachof the individual cell voltages (see equations in FIG. 6). Each ITO filmis separated by high resistance glass so each cell is electricallyseparate. For the next layer, a semi-transparent n-type semiconductorwindow (CdSe, ZnO, etc.) was used. This layer also has low conductivity,so the material can be deposited as a continuous film overlapping eachcell. If this layer is more conductive (i.e. CdS, Al-doped ZnO) theoffset blocks in FIG. 5B would need to be separated. The active layer(p-type CdTe) also has low conductivity and can be sprayed as acontinuous rectangle patch for simplicity (FIG. 5D). The solutiondeposited metal contact (Au/Ag) only comes in contact with Layer 3(CdTe) of the cell and Layer 1 (ITO) of the adjacent cell. This preventsshorting pathways for the photogenerated charge.

An example of a panel is shown in FIG. 6 where the number of modulesconnected in series determines the maximum voltage and the number ofmodules connected in parallel determines the maximum current. In thiscase, a series connection (labeled S in the Figure) of two parallelmodules (P) can create a total voltage that is the sum of 16 cells(VT=V1+V2) and a total current that is the sum of 2 modules (IT=I1+I2).Additional series or parallel connections (not shown) can be added toamplify the voltage or current, respectively. In addition, larger deviceareas produce larger currents, and in this way the masking pattern canbe manipulated to build a module with specific power requirements inmind. Given the flexible nature of this design, spray processed thinfilm solar modules can be fabricated using the appropriate layer maskson a variety of substrates. Preliminary test devices produced over 4.0V, 20 μA in room light with the configuration shown in FIG. 6 usingITO/CdSe/CdTe/Au on four 1 in×3 in glass microscope slides. Flatrectangular glass was used, however, curved or irregular shapes could beused as a substrate. This serpentine masking pattern can also bemodified to use a circular or spiral geometry (i.e., to produce curvedmodules) as long as the basic design remains the same. Flexible plasticsubstrates may also be used if the film annealing temperatures arebrought below the melting point of the substrate (T≈250° C.).

Solution processing offers a vital cost reduction due to the addedpotential advantage of high throughput roll to roll printing on largeand flexible surfaces.

Another opportunity arises with this design where the cells can also beinverted to spray a module onto non-transparent substrates (for examplemetal, ceramic, etc.). In this case, the reflective metal contact shouldbe deposited first followed by the active layers and finally atransparent conductive top contact. This top layer could be solutionprocessed transparent metal oxides (like ITO) or transparent metallicfilms (metal nanowires, graphene, carbon nanotubes). Additionally, anycombination of p/n materials could be used here and is not limited toCdSe or ZnO/CdTe. A specific architecture and spray deposition procedureis described in U.S. patent application Ser. Nos. 14/051,226 and14/051,134, both filed on Oct. 10, 2013 that is compatible with both thesolution ITO and the masking procedure disclosed here. Theseapplications are incorporated herein by reference for teachingdeposition techniques.

In summary, disclosed here is a unique composition of matter forsolution processing of indium tin oxide films which takes advantage ofthe removal of organic content and optimized component concentrations toproduce superior quality ITO films with less processing time. This newformula enabled the construction of a solar cell made entirely ofair-stable solution processed materials, thus allowing processing undernormal atmospheric pressure and avoiding the need for more costly andcomplex techniques involving vacuum and/or evaporation. Manipulation ofliquid material solutions facilitates spraying, spin-coating,dip-coating deposition procedures to produce electronic devices withsubstantially reduced net device costs when compared to conventionaltechniques. The top-to-bottom solution processed solar cell design wasapplied to development of an innovative ordering of device layers forscalable solar module designs based on a series of masking patterns.

CONCLUDING REMARKS

Described herein is an improved formula for solution processed ITO whichproduces spin coated or spray cast transparent conductive oxide filmswith enhanced properties and greatly reduced the processing time ofabout one fifth of conventional techniques. The improved formula wasapplied with other solution components to produce an entirely solutionprocessed solar cell prepared from inorganic materials. Solutionprocessing can lead to lower fabrication costs and ease of depositiononto large and irregular surfaces. The module design can be applied tothese surfaces to produce on-site power sources with simple masking of alayer-by-layer deposition.

The improved formula for ITO combustion synthesis can be applied toother metal oxides for a wide variety of optoelectronic applications.For other cell architectures, the masking can be applied to singlejunction cells with one low work function metal contact, or the modulelayers can be reversed (with the reflective metal contact as the bottomlayer) to deposit a solar module onto any desired surface that iscompatible with the processing conditions.

All documents mentioned herein are hereby incorporated by reference forthe purpose of disclosing and describing the particular materials andmethodologies for which the document was cited.

Although the present invention has been described in connection withpreferred embodiments thereof, it will be appreciated by those skilledin the art that additions, deletions, modifications, and substitutionsnot specifically described may be made without departing from the spiritand scope of the invention. Terminology used herein should not beconstrued as being “means-plus-function” language unless the term“means” is expressly used in association therewith.

REFERENCES

-   1. Kim, M. G., et al., Low-temperature fabrication of    high-performance metal oxide thin-film electronics via combustion    processing. Nature Materials, 2011. 10(5): p. 382-388.-   2. Ellmer, K., Past achievements and future challenges in the    development of optically transparent electrodes. Nature    Photonics, 2012. 6(12): p. 808-816.-   3. Javier, A. and E. E. Foos, Nanocrystal Photovoltaic Paint Sprayed    With a Handheld Airbrush. IEEE Transactions on Nanotechnology, 2009.    8(5): p. 569-573.-   4. Olson, J. D., et al., CdTe Schottky diodes from colloidal    nanocrystals. Applied Physics Letters, 2010. 96(24): p. 242103.-   5. Bezryadina, A., et al., Mid-gap trap states in CdTe nanoparticle    solar cells. Applied Physics Letters, 2012. 100(1): p. 013508.-   6. Barkhouse, D. A. R., et al., Device characteristics of a 10.1%    hydrazine-processed Cu2ZnSn(Se,S)4 solar cell. Progress in    Photovoltaics: Research and Applications, 2012. 20(1): p. 6-11.-   7. Gur, I., et al., Air-stable all-inorganic nanocrystal solar cells    processed from solution. Science, 2005. 310(5747): p. 462-465.-   8. Jasieniak, J., et al., Solution-Processed Sintered Nanocrystal    Solar Cells via Layer-by-Layer Assembly. Nano Letters, 2011.    11(7): p. 2856-2864.-   9. Debnath, R., O. Bakr, and E. H. Sargent, Solution-processed    colloidal quantum dot photovoltaics: A perspective. Energy &    Environmental Science, 2011. 4(12): p. 4870-4881.-   10. Chen, C.-C., et al., Visibly Transparent Polymer Solar Cells    Produced by Solution Processing. ACS Nano, 2012. 6(8): p. 7185-7190.-   11. Park, B., Y. Chan Kim, and S. H. Yun, All-solution-processed    inverted polymer solar cells with low temperature, water-processable    hybrid electron-collecting layers. Journal of Materials Chemistry    A, 2013. 1(6): p. 2030-2038.-   12. Nanu, M., J. Schoonman, and A. Goossens, Nanocomposite    Three-Dimensional Solar Cells Obtained by Chemical Spray Deposition.    Nano Letters, 2005. 5(9): p. 1716-1719.-   13. Todorov, T. K., et al., Solution-processed Cu(In,Ga)(S,Se)2    absorber yielding a 15.2% efficient solar cell. Progress in    Photovoltaics: Research and Applications, 2013. 21(1): p. 82-87.-   14. Ju, T., L. Yang, and S. Carter, Thickness dependence study of    inorganic CdTe/CdSe solar cells fabricated from colloidal    nanoparticle solutions. Journal of Applied Physics, 2010.    107(10): p. 104311.-   15. Sun, S., et al., Controlled synthesis of CdTe nanocrystals for    high performanced Schottky thin film solar cells. Journal of    Materials Chemistry, 2012. 22(36): p. 19207-19212.-   16. MacDonald, B. I., et al., Layer-by-Layer Assembly of Sintered    CdSexTe1−x Nanocrystal Solar Cells. ACS Nano, 2012. 6(7): p.    5995-6004.-   17. Ming-Yi, L., et al. All-solution-processed-inverted polymer    solar cells on PET substrates with CuOx thin film as an anode    interlayer. in Photovoltaic Specialists Conference (PVSC), 2010 35th    IEEE. 2010.-   18. Tung, V. C., et al., Towards solution processed all-carbon solar    cells: a perspective. Energy & Environmental Science, 2012. 5(7): p.    7810-7818.-   19. Kim, T.-S., et al., All-solution-processed ITO-free polymer    solar cells fabricated on copper sheets. Solar Energy Materials and    Solar Cells, 2012. 98(0): p. 168-171.-   20. Foos, E. E., et al., Inorganic photovoltaic devices fabricated    using nanocrystal spray deposition. ACS Applied Materials &    Interfaces, 2013, 5, 8828

What is claimed is:
 1. A composition for forming indium tin oxide (ITO),the composition consisting essentially of: a solution of a tin salt, anindium(III) salt, ammonium nitrate, ammonium hydroxide, and a solvent of2-methoxyethanol or water, wherein, upon heating in a solution, thecomposition is capable of forming a substantially transparent ITO filmhaving a sheet resistance of <300 Ω/sq.
 2. The composition of claim 1,wherein the tin salt is tin chloride and the indium(III) salt isindium(III) nitrate, each present in a weight percent ratio of about15%: 85%, respectively, measured in terms of SnCl₂.2H₂O andIn₂O₃.2.85H₂O.
 3. The composition of claim 1, wherein the solvent is2-methoxyethanol.
 4. The composition of claim 1, wherein the solvent iswater.
 5. The composition of claim 4, free of hydrocarbons.
 6. Acomposition for forming metal oxides, the composition consistingessentially of: a solution of a nitrate of zinc, indium, or aluminum,optionally tin chloride, ammonium nitrate, ammonium hydroxide, and asolvent of 2-methoxyethanol or water, wherein the composition is capableof forming zinc tin oxide (ZTO), indium oxide (IO), indium zinc oxide(IZO), cadmium tin oxide (CTO), aluminum zinc oxide (AZO), or zinc oxide(ZO).
 7. A method of creating indium tin oxide (ITO), the methodcomprising: forming a layer of a solution consisting essentially of atin chloride, an indium(III) nitrate, ammonium nitrate, ammoniumhydroxide, and a solvent of 2-methoxyethanol or water; and heating thelayer to form ITO having a sheet resistance of <300 Ω/sq.
 8. The methodof claim 7, further comprising spraying or casting the solution onto asubstrate prior to the heating.
 9. The method of claim 7, furthercomprising forming additional layers from solution to create anoptoelectronic device.
 10. The method of claim 9, wherein a mask isemployed to pattern individual layers.
 11. The method of claim 10,wherein said optoelectronic device is a solar cell.
 12. The method ofclaim 10, wherein said mask is employed in conjunction with a flexiblesubstrate.
 13. The method of claim 12, wherein said optoelectronicdevice is a solar cell.
 14. The method of claim 9, first comprisingdepositing a reflective metal contact onto a non-transparent substrate.15. The method of claim 9, wherein said optoelectronic device is a solarcell.
 16. The method of claim 15, wherein masks are employed to patternlayers of different materials thereby forming a module comprising aplurality of cells electrically connected in series.
 17. The method ofclaim 16, wherein said module is a solar module.